- ALKALİ-SİLİKA REAKSİYONU TEST KABİNİ
ALKALİ-SİLİKA REAKSİYONU TEST KABİNİ
ASR TEST SYTEMSCHLEIBINGER-GERMANY (KODFRK 001)
For storage of concrete specimen at 60°C and nearly 100% rel. humidity. Temperature profiles are free programmable. With color touch screen for control and graphic data display. Integrated data-logger, Etherenet / TCP/IP interface for remote control via WeB-browser.


Spezifications:
 Temperature range: room temperature to max. 65 °C
 Temperature stability: < 1 K (for closed system)
 Inside dimensions (l x w x h): 150 x 109 x 67 cm,
 Outside dimensions (l x w x h): 185 x 158 x 122 cm
 Weight: 460 kg (empty state)
 Water content: 280 liters
 Insulation: rigid foam 50 mm
 2 lids with torque compensated hinges, insulated, with lid selant
 Removable grating for 600 kg of load

 water outflow: 1/2´´
 Heating Power: 2 x 6 kW
 Interior is made of stainless steel
 Savety devices: temperature limiter, power switches, residual current circuit breakers.


ASR Fog-System

( 1 Pcs. )

Fog-generating system for the ASR reactor.
With a high pressure pump and special stainless steel nozzles.
The size of the droplets is smaller then 30 micron.
The fog function is freely adjustable via a control in "duration" or "interval".
ASR Specimen Container
( 1 Pcs. )
For 3 specimen with a size of 75 x 75 x 280 mm.
Inner size (l x w x h): 280 x 130 x 400 mm.
Made of 1,5 mm thick stainless steel, complete welded, pickled and passivated.


Lid with drip-down tin. Removable grating for concrete specimen at 50mm level.




Specimen spacers at 260 mm height.
Weight approx. 6.5 kg.
ASR Specimen Mould, stainless steel
( 1 Pcs. )
for the production of one specimen with the size of 75 x 75 x 280 mm. Made of 10 mm stainless steel. Incl. lid made of stainless steel for covering the sample during the hydration. Incl. 2 anchors and fixing screws for the length change measurement.
Dial Gage Measurement Stand ASR, with Digital Probe
( 1 Pcs. )
for determination of the length change of concrete specimen with the size of 75 x 75 x 280 mm or cylinders with the size of 150 x 300 mm.
 With a depression in the base for a 10 mm ball.
 Incl. digital probe Mitutoyo ID-H with a resolution of 0.5 mikron and an accuracity of 1.5 mikrons.
 Incl. carbon fiber reinforced reference bar with the size of 280 mm.
Other sizes, probes and measuring tap on request.
Reference Anchor for the ASR Specimen
( 2 Pcs. )
For concreting in the sample.
14 x 16 mm hexagon bolt, central hole M5 (5mm) with a countersink of 9 mm x 45°, stainless steel 1.4571 / V4A.
Packaging ASR-Reactor
( 1 Pcs. )

wooden box heat treated according to regulations ISPM15/IPPC
box dimensions: 200 x 170 x 165 cm, weight: 820 kg
and additional pallet: 120 x 80 x 50 cm, weight: 150 kg



Deutscher Ausschuss für Stahlbeton, DAfSTb (Hrsg.): Vorbeugende Maßnamen gegen schädigende Alkalireaktionen im Beton: Alkali-Richtlinie, Anhang B, Teil3, Berlin: Beuth, 2007
Standard NF P18-454 (Décembre 2004) : Béton - Réactivité d'une formule de béton vis-à-vis de l'alcali-réaction - Essai de performance - Reactivity of concrete for alkali-silica Performance test
RILEM Test Method TC 191-ARP (Ed.): AAR-4.1: -Detection of Potential Alkali-Reactivity-60°C Accelerated method for testing aggregate combinations using concrete prisms - Bagneaux, 2006
ASTM C1567 -8 : Standard Test Method forDetermining the Potential Alkali-Silica Reactivity ofCombinations of Cementitious Materials and Aggregate
(Accelerated Mortar-Bar Method)
ASTM C1293 -08b: Standard Test Method forDetermination of Length Change of Concrete Due to Alkali-Silica Reaction1
Cihaz RILEM/TC-ARP/01/20 ve ASTM C 1293 standartlarına uygun olarak birbir uygun olarak dizayn edilmiş çok spesyal bir test cihazıdır..
Alkali – Silika Reaksiyonu, çimentodaki alkali ile agregalardaki aktif silis ve nem sonucu oluşur. Aktif silis, alkali ve nemin bir araya gelmesiyle reaksiyona girerek jel kıvamında alkali silikat bileşikleri oluşturmaktadır. Bu bileşikler beton içinde şişme yapmaktadır ve betonun çatlamasına neden olan bir oluşum sürecini başlatmaktadır. Alkali – silika reaksiyonu uzun ve devamlı bir süreçtir ve çatlaklar oluştuktan sonra ise kesin bir çözümü yoktur. Bu reaksiyonuna karşı alınacak önlemlerin betonun dizaynı aşamasında uygulanması gerekmektedir.
ASR Test Kabini içerisinde beton numuneleri yaklaşık %100 rölatif nem, 20 C ile 70 C arasında muhafaza edilmektedir. Sıcaklık sapması 0.5K 'dan daha hassastır. Sıcaklık sürekli olarak kayıt edilmekte ve grafiksel olarak gösterilmektedir.
ASR Numune Kabı 2 mm kalınlığında paslanmaz çelikten imal edilmektedir ve iç ebadı 280 x 130 x 400 (boy – en – yükseklik) cm 'dır. Opsiyonel ASR Buhar Oluşturma Sistemi 40 C 'den düşük sıcaklıklarda veya düşük su
sıcaklıklarında kullanılabilen buhar sistemi %100 nem oluşturabilmektedir ve yüksek basınçlıpompası ve paslanmaz çelik püskürtme memesi ile birlikte temin edilmektedir. 1.2 litre / saat kapasitelidir.
Uygulama; ASR Numune Kaplarını 60 C ve yaklaşık %100 rölatif nem altında tutmaktır.
Ebadı; 1500 x 1100 x 950 mm (boy – en – yükseklik)
Su Seviyesi; 190 mm Test Kabı Rafı; 2 adet İç Kabin; Paslanmaz çelik Kapak; Tork kompanzasyon menteşeli 750 x 120 Sensör; RTD PT100 1/10 DIN B Isıtma; 2 x 6 kW 3*230 V (veya 400 V) aşırı sıcaklık korumalı Kontrolör – ısıtıcı; 2 sabit seviyeli röle 3 faz; Duvara montaj edilebilen kabin Kullanıcı Arabirimi; Renkli dokunmatik ekran ve online grafikli
Arabirim; Ethernet TCP/IP kontrol ve veri toplama amaçlı
Ağırlık; 500 kg Elektrik Bağlantısı; 3 * 32 A 230 / 400 V, CEE fişli

CİHAZIN
BİLİMSEL ÇALIŞMLARDA KULLANILDIGI BAZI KURUMLAR
• VDZ (German Central Cement Research Inst) Düsseldorf, Germany
• basf Trostberg, Germany
• University Bochum, Germany
• IMP Switzerland
• EMPA (Federal Swiss Material Testing Institute) Zürich, Switzerland
• BAM (Federal German Materials testing institute) Berlin, Germany
• Technical University Hamburg, Germany
• CEMEX Germany
• Erft Labor etc